Adhesives for wood Woodmax TC 24.50, class D4

Two component adhesive based on the modified vinyl polyacetate dispersion, with water resistance class D4 according to PN-EN 204. The joint, after achieving full strength, offers very good adhesion to wooden surfaces subjected to static and dynamic load and ensures good initial adhesion.

The adhesive has been certified by IFT of Rosenheim, acknowledging the D4 class according to PN-EN 204, and high thermal resistance: ≥ 7 N/mm2 according to EN 14257 (WATT`91).


  • Bonding solid wood for production of interior joinery;
  • Bonding soft wood;
  • Bonding hard wood;
  • Bonding floor panels;
  • Bonding particleboards and fibreboards;
  • Bonding plywood;
  • Bonding other wood-based material;
  • For use in cold press and manual bonding;
  • For use in hot press, for bonding veneer and laminate to particle boards and MDF.


Material preparation

The surface to be bonded must be dry cleaned and free from dust, without traces of oils and fats that would impair adhesion. Wood humidity should be 10 to 14 [%]. The elements to be bonded should be matched to each other.

Adhesive application

Stir the adhesive carefully before use. The adhesive can be applied to one or both sides with a brush, spatula, bottle dispenser, applicator, hand roller or machine (using the nozzle or roller).The recommended amount of adhesive applied, depending on the type of surface, is 90 to 180 [g/m2].


The adhesive does not cause discolouration of wood, but it is recommended to avoid tools containing iron; in contact with wood containing tannin it may cause discolouration.

Open time

Open time: 3 ÷ 10 [min]. The open time depends on the porosity of the wood, amount of adhesive applied, humidity and temperature of air, adhesive and bonded elements.

Bonding temperature

Use in temperatures 15 [°C] ÷ 30 [°C]. Applies to the ambient temperature, especially the temperature of the material bonded and the adhesive.


Pressing pressure — in the range 0.1 to 1.2 [N/mm2] according to the stress occurring in the bonded materials. In case of manual application, the press the surfaces to be bonded together to squeeze out the adhesive excess.

Pressing time — depends on the type of wood and its moisture content, temperature and relative humidity of air and the amount of adhesive applied and the stresses occurring in the bonded materials. The bonded components should be pressed until the strength allowing transport or further processing is achieved.

Average pressing times suggested:

  • Cold press 15 ÷ 30 [min];
  • Hot press 2 ÷ 10 [min] (depending on press temperature).

Good results can be achieved wile bonding observing the following conditions:

Bonding temperature 15 ÷ 25 [°C]
Relative air humidity 40 ÷ 70 [%]
Wood humidity 10 ÷ 14 [%]
Amount of adhesive applied 90 ÷ 180 [g/m2]
Maximum open time 3 ÷ 8 [min]


Wash the tools in water immediately after completing the work. Do not allow the adhesive to dry out. Mechanically remove dried adhesive from tools after soaking in hot water for (about 1 hour).


Product is available in 20 kg, 60 kg and 1000 kg plastic containers.

The packaging and transportation are not subject to RID/ADR regulations. Other container can be provided upon agreement between the manufacturer and customer. The packaging may not affect the quality of product.


Store in original, tightly closed containers at a temperature of +7 to +30 [°C]. Under these storage conditions, product retains its properties for 12 months from date of manufacture.